The main performance parameters are shown in Table
| Serial number | Test items | Unit | Test Standard | SR No. | |||
| SR 35-A | SR 40-A | SR 50-A | SR 60-A | ||||
| 1 | Hardness | Shore A | GB/T531.1-2008 | 35±7 | 40±10 | 50±10 | 60±10 |
| 2 | Density | g/cm3 | 4.3.2 | 0.8≤μ±3σ≤1.4 | 1.00≤μ±3σ≤1.51 | 1.00≤μ±3σ≤1.51 | 1.1≤μ±3σ≤1.5 |
| 3 | 25℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.25≤μ±3σ≤0.75 | 10%: 0.45≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.63≤μ±3σ≤1.77 | 20%: 0.95≤μ±3σ≤1.45 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.20≤μ±3σ≤2.24 | 30%: 1.50≤μ±3σ≤2.50 | ||||
| 4 | 25℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 5 | 25℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 6 | -30℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.08≤μ±3σ≤.0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.65 | 10%:0.55≤μ±3σ≤0.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.90≤μ±3σ≤1.20 | 20%:1.10≤μ±3σ≤1.95 | ||||
| 30%:0.45≤μ±3σ≤0.9 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.50≤μ±3σ≤2.00 | 30%: 2.00≤μ±3σ≤3.95 | ||||
| 7 | -30℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 8 | -30℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 9 | 60℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.70 | 10%: 0.35≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.80≤μ±3σ≤1.30 | 20%:0.65≤μ±3σ≤1.60 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.00≤μ±3σ≤2.10 | 30%: 1.00≤μ±3σ≤2.50 | ||||
| 10 | 60℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 11 | 60℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 12 | Double 85 post-aging compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.50≤μ±3σ≤0.70 | 10%: 0.40≤μ±3σ≤1.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.90≤μ±3σ≤1.30 | 20%: 1.00≤μ±3σ≤3.20 | ||||
| 30%:0.45≤μ±3σ≤0.75 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.40≤μ±3σ≤2.10 | 30%: 1.70≤μ±3σ≤5.50 | ||||
| 13 | Double 85 post-aging shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 14 | Double 85 post-ageing Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 15 | Compression curve after high and low-temperature cycle | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.45≤μ±3σ≤0.65 | 10%: 0.50≤μ±3σ≤2.20 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.85≤μ±3σ≤1.35 | 20%: 1.00≤μ±3σ≤4.00 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.30≤μ±3σ≤2.50 | 30%: 1.80≤μ±3σ≤6.80 | ||||
| 16 | Shear performance under pressure after high and low temperature | MPa | ASTM C273C /273M-16 | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 |
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 17 | Tensile strength after high and low-temperature cycle | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 18 | Flame retardant | / | UL94 | UL94 V0(2mm) | V0(t≥2mm) | V0(t≥2mm) | V0(t≥2mm) |
| V1(1≤t＜2mm) | V1(1≤t＜2mm) | V1(1≤t＜2mm) | |||||
| HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | |||||
| 19 | Forbidden object | / | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV |
| 20 | Insulation | MΩ | 1000V DC 60s | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 |
| 21 | Impedance | mA | 2700V DC 60s | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 |
| 22 | Thermal conductivity | W/(m·K) | GB/T 10295-2008 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 |
| 23 | Specific heat capacity | J/(g·K) | ASTM E1269-2011 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 |
| 24 | Stress retention rate | % | GB/T1685-2008 | ≥40 | ≥40 | ≥40 | ≥40 |
| 25 | 25℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.8 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 26 | -30℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 27 | 60℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥0.6 | Min≥1.5 |
| 28 | Double 85 ageing shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 29 | Shear strength after high and low-temperature cycles with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |